Ion implantation in GaN at liquid-nitrogen temperature: Structural characteristics and amorphization

C. Liu, B. Mensching, M. Zeitler, K. Volz, and B. Rauschenbach
Phys. Rev. B 57, 2530 – Published 15 January 1998
PDFExport Citation

Abstract

This paper deals with the results of a systematic investigation of damage generation and accumulation until amorphization induced by 180 keV Ca+ and Ar+ implantation in GaN films at liquid-nitrogen temperature. The structure of GaN films before and after implantation was characterized by Rutherford backscattering/channeling, cross-sectional transmission electron microscopy, and high-resolution x-ray diffraction. The as-implanted GaN films exhibits an expanded lattice. Its texture was determined by pole figure measurement. An amorphous component has been found after Ca+ implantation at doses not less than 3×1014cm2. This suggests that Ca+ implantation for p-type doping be carried out below this dose, in order to avoid unrecoverable structural damage and to achieve better transport properties. On the other hand, implantation with higher doses is generally needed to compensate for the native electron background of GaN and to realize p-type reversal. This conflict uncovers the essential difficulty for p-type doping of GaN by ion implantation. The maximum damage concentration exists in a depth of 100 nm below the surface, which corresponds to the mean projected range, and broadens gradually towards surface and greater depth with increasing ion fluence. The thresholds for the amorphization of GaN films are revealed to be 6×1015cm2 for both Ca+ and Ar+ implantation. The amorphization mechanism is discussed and the accumulation of amorphous clusters seems to be the reason for the collapse of GaN crystalline.

  • Received 25 September 1997

DOI:https://doi.org/10.1103/PhysRevB.57.2530

©1998 American Physical Society

Authors & Affiliations

C. Liu*, B. Mensching, M. Zeitler, K. Volz, and B. Rauschenbach

  • Institut für Physik, Universität Augsburg, D-86135 Augsburg, Germany

  • *Permanent address: Department of Physics, Wuhan University, Wuhan 430072, People’s Republic of China. Electronic address: chang.liu@physik.uni-augsburg.de

References (Subscription Required)

Click to Expand
Issue

Vol. 57, Iss. 4 — 15 January 1998

Reuse & Permissions
Access Options
Author publication services for translation and copyediting assistance advertisement

Authorization Required


×
×

Images

×

Sign up to receive regular email alerts from Physical Review B

Log In

Cancel
×

Search


Article Lookup

Paste a citation or DOI

Enter a citation
×