Self- and foreign-atom diffusion in semiconductor isotope heterostructures. II. Experimental results for silicon

H. Bracht, H. H. Silvestri, I. D. Sharp, and E. E. Haller
Phys. Rev. B 75, 035211 – Published 17 January 2007

Abstract

We report the diffusion of boron, arsenic, and phosphorus in silicon isotope multilayer structures at temperatures between 850°C and 1100°C. The diffusion of all dopants and self-atoms at a given temperature is modeled with the same setting of all native-point-defect-related parameters. The evaluation of the relative contributions of charged native-point defects to self-diffusion enables us to determine the defect energy levels introduced by the native-point defects in the Si band gap. Making allowance for the fact that the band gap and the energy levels change with temperature, an energy-level diagram of the native-point defects is obtained that shows a reversed level ordering for the donor levels of the self-interstitials. In accord with the general state of knowledge, the diffusion of boron is mainly mediated by self-interstitials whereas the properties of both vacancies and self-interstitials are important to model arsenic and phosphorus diffusion. The simultaneous diffusion of phosphorus and silicon requires the existence of a singly positively charged interstitial phosphorus. It is the diffusion of this defect that strongly affects the shape of the phosphorus diffusion tail and not entirely the supersaturation of self-interstitials argued so far. Taking into account the mechanisms of dopant diffusion and the properties of native-point defects determined from the simultaneous diffusion experiments, let us describe accurately dopant profiles given in the literature. Altogether, this work provides overall consistent data for modeling dopant and self-diffusion in Si for various experimental conditions. A comparison of experimentally and theoretically determined activation enthalpies of self- and dopant diffusion shows excellent agreement for self-interstitial-mediated diffusion but significant differences for vacancy-mediated diffusion in Si. This disagreement either reflects the deficiency of first-principle calculations to accurately predict the energy band gap of Si or points to a still-remaining lack in our understanding of diffusion in Si.

  • Figure
  • Figure
  • Figure
  • Figure
  • Figure
  • Figure
  • Figure
11 More
  • Received 15 September 2006

DOI:https://doi.org/10.1103/PhysRevB.75.035211

©2007 American Physical Society

Authors & Affiliations

H. Bracht*

  • Institut für Materialphysik, University of Münster, D-48149 Münster, Germany

H. H. Silvestri, I. D. Sharp, and E. E. Haller

  • Lawrence Berkeley National Laboratory and University of California at Berkeley, Berkeley, California 94720, USA

  • *Electronic address: bracht@uni-muenster.de

See Also

Article Text (Subscription Required)

Click to Expand

References (Subscription Required)

Click to Expand
Issue

Vol. 75, Iss. 3 — 15 January 2007

Reuse & Permissions
Access Options
Author publication services for translation and copyediting assistance advertisement

Authorization Required


×
×

Images

×

Sign up to receive regular email alerts from Physical Review B

Log In

Cancel
×

Search


Article Lookup

Paste a citation or DOI

Enter a citation
×